Tanaka develops manufacturing process for platinum

Tanaka, the developer of industrial precious metals, claims to have made the world’s first bulk platinum with controlled crystal grain size in the nano scale.

The average grain size of a typical bulk metal is about 10 µm at the smallest. In this new technology, the average crystal grain size can be controlled in the nano scale. As a result, the developed pure platinum, with 99.9% or higher purity, has 10 times the hardness and 4 times the strength of typical platinum materials.

It is known that the properties of metals, including precious metals, are enhanced by grain refinement. In recent years, steel and nonferrous metals with nano-sized crystal grains have been produced by deformation processing to apply extreme levels of plastic deformation⁵ and recrystallize their structures.

While deformation processing temporarily hardens metal materials, when highly pure precious metal materials undergo the same process, the arrangement of atoms that form their crystalline structure changes and new crystal grains are nucleated and grown over periods of a few hours to a few days. As a result, the hardness of the material noticeably decreases (softens), and it has been very difficult to refine the crystal grains through deformation processing.

The hardness and strength of the platinum materials manufactured by this technology are much higher than those of typical platinum materials.

The developed platinum has a high density of small-angle grain boundaries, large-angle grain boundaries, dislocations, and other lattice defects within the material.

Therefore, the developed platinum has properties that are clearly different from the properties of commonly known platinum materials, even without additive elements or alloying.

As a new material with high purity and high functionality, it is expected to be applied to a wide field of industries, including the electronics and aerospace industries.

1. World’s